::: Ceramic Raw Materials :::

Our Products


Alumina Ball:
Alumina BallPurpose:
This product is of high hardness, big density, good normalization behavior that used in paint, table ware, chemical, tiles industry etc.

Specification

CHEMICAL COMPOSITION:     PHYSICAL CHARACTERISTICS
Al2O3 91.1%     Specific Gravity             3.6-3.7 gr/cm3
SiO2 5.4% Porosity 0%
MgO  1.24%     Hardness 9moh's
CaO  0.78%     Bending Strength 166 ? 16 MPa
Na2O 0.20%   Elasticity Modulus  124 ? 7 GPa
K2O  0.02%     Color  White


Body Stain:
Body StainPurpose:
The reasons for using a stain versus an oxide, etc. are (1) Stability of Color — an important criteria for tiles, sanitary ware, etc. (2) Insolubility — an insoluble (in water) stain greatly diminishes the risk in handling wet glazes when dipping or pouring, etc. (3) Color — the fired color of most stains is identical to the raw color because it has already been fired.

Specification

CHEMICAL COMPOSITION:
CP-RO31 Al2O3 90% ? 10%
MnO 10% ? 4%
     
CP-NA22 TiO2 79% ? 10%
Sb2O3 13% ? 3%
Cr2O3 8% ? 3%

 


Ceramic Pigment:
Ceramic PigmentPurpose:
Application in tableware, sanitary ware, tiles & glass industry for double fast firing, Porosa and Gres.

Specification:

|
PARTICLE SIZE: Particle Size on 45 microns ≤1.5%
Recommended Use:
 

Floor tile & Wall tile Can be used with all glaze compositions,but it is favourable the formulations with zincMixable with all other pigments Maximum recommended temperature: 1250oC.


 

Calcined Alumina:
Calcined AluminaPurpose:
Calcined alumina is aluminum oxide that has been heated at temperatures in excess of 1,050? C (1,900? F) to drive off nearly all chemically combined water. In this form, alumina has great chemical purity, extreme hardness, high density, and a high melting point.

Specification

Chemical Analysis
Na2O % 0.35
SiO2 1 % 0.011
Fe2O3 % 0.011
LOI % 0.47

 

Engobe Ball:
Engobe BallPurpose:
Engobes can be defined as liquid clay slips of varying compositions which are applied to the surface of a clay object, e.g. a pot. The purpose of the engobe can be as different as the varied forms it comes in: to give color to a piece; to improve the surface texture; to provide a ground to do further decoration on.

Specification

CHEMICAL ANALYSIS: Ultimate analysis (per cent)
SiO2 65.8
TiO2 1.6
Al2O3 22.1
Fe2O3 0.9
Ca0 0.1
Mg0 0.3
K20 2.1
Na20 0.3
Loss on Ignition at 950oC 6.8

CALCULATED MINERALOGICAL COMPOSITION:
Kaolinite 35
Potash Mica 18
Soda Mica  4
Quartz   33

PARTICLE SIZE DISTRIBUTION:
Equivalent Spherical Diameter
Microns: 1 2 5 10 20
% Undersize 58 67 82 89 92

 

Ball Clay:
Ball ClayPurpose:
Ball clays are used in homogeneous ceramic bodies, porcelains, stonewares, sanitary wares, casting slips, pressing bodies etc. because of their plastic nature combined with high firing temperature. Ball clays have very high dry shrinkage combined with high green strength and slow drying.

Specification

MINERAL CONTENT:
Quartz, Kaolinite and Mica CHEMICAL CONTENT:
  Persero Method
Iron Trioxide (Fe2O3) 1.00 – 1.30% ICP
Alumina Trioxide (AL2O3) 21.00 – 27.00 % IC
Calcium Oxide (CaO) 0.03 – 0.06% ICP
Magnesium Oxide (MgO) 0.30 – 0.90% ICP
Manganese Dioxide (MnO2) 0.01% ICP
Chromium Trioxide (Cr2O3) 0.01 – 0.02% ICP
Sodium Oxide (Na2O) 0.05 – 0.20% ICP
Potassium Oxide (K2O) 1.20 – 2.00% ICP
Silicon Dioxide (SiO2) 60.01 – 75.00% Gravimetric
Titanium Dioxide (TiO2) 0.01 – 1.20% ICP
Loss On Ignition (LOI) 6.00 – 7.80% Gravimetric
Moisture Content (MC) 20.00 – 27.00% Gravimetric

 

Kaolin:
KaolinPurpose:
A fine, pure-white clay (hydrated aluminum silicate) used in porcelain teeth & sanitary ware.

Specification

Analysis Specification Control Method
    Value*  
Humidity ≤14% 11.7 G MA QA BRE 10
Residues > a45? ≤ a 300 ppm 91 G MA QA BRE 14
Casting Density ≥ a 1.64 ≥ a 1.64 G MA QA BRE 05
< 2 ? 46 a 58% 46 a 58% G MA QA BRE 04
Fe2O3 0.6 a 1.0% 0.6 a 1.0% G MA QA BRE 01
* G = Guaranteed value, I = Indicative value

 

Potash Feldspar Chips (0-6 mm):
Potash Feldspar ChipsPurpose:
Potash feldspar is a substance that is used is ceramic & granite tiles & sanitary ware & table ware.

Speciation

Chemical Analysis (Typical values on a % dry basis, onless stated)
SiO2                                66%
Al2O3 18.00 +/- 1.00
Fe2O3 0.11 +/- 0.02
TiO2  0.02 +/- 0.01
CaO 0.25 +/- 0.10
Na2O 3.00 +/- 0.50
K2O 11.50 +/- 0.5
Moisture 2% typical
Particle Size (Measured Value)  
Chips Passing 5 mm 95% max
Passing 1 mm 4% typicall
   
Other Information:  
Packaging: Bulk  

Potash Feldspar Powder:
Potash Feldspar PowerPurpose:
Potash feldspar is a substance that is used is ceramic & granite tiles & sanitary ware & table ware.

Printing Paste:
Printing PastePurpose:
Printing paste is a serigraphic printing paste that is homogeneous glassy compound crystalline powder used in ceramic industry.

Specification


Chemical Composition
Oxides Percentage
SiO2 45.00 – 58.00%
Al2O3 5.00 – 20.00%
CaO, MgO, 13.00 – 25.00%
ZnO, 0 – 4 %
BaO 0 – 2%
K2O, Na2O 3.00 – 5.50%
B2O3 1.0 – 4.50%
ZrO2 25.00 – 30.00%
   
Particle Size :
Particle Size on 45 microns   : 0.1 – 05%

 

Quartz Powder:
Quartz PowderPurpose:
Quartz powder is a kind of product that used in tiles, tableware & sanitary ware industry.

Specification

SiO2 + 99.0%
Fe2O3 0.1% maximum

 

Sodium Feldspar Chips (0-6 mm):
Sodium Feldspar ChipsPurpose:
Sodium feldspar is one of the largest consumed products in Asia homogeneous tiles industry.

Specification

SiO2 68-72
Al2O3 17.50 +/- 1.00
Fe2O3 0.23 +/- 0.02
TiO2 0.25 +/- 0.02
CaO 1.25 +/- 0.25
Na2O 7.50 +/- 0.25
K2Oo:p> 0.50 Typ
   
L* value 78.00 +/- 1.00
a* value 0.80 +/- 0.10
b* value 16.00 +/- 0.50

 

Sodium Feldspar powder:
Sodium Feldspar PowerPurpose:
Sodium feldspar is one of the largest consumed products in Asia homogeneous tiles industry.

Specification

Na2O  10% ? 1.0%
K2O 2.5%  0.5%
SiO2 70% ? 1.0%

 

STPP
STPPPurpose:
STPP mainly used in the slip of building ceramics, tiles, tableware and sanitary ware etc.

Specification

   
Na3P3O10 (wt min) 25 – 35%
P2O5 (wt min) 14.25 – 20.00 %
PH Value 09.00 – 14.00%
Water Insoluble (wt max) 0.05%
Whiteness (min) 50 – 100%
Fe (Max) 0.02%
Bulk density (GR/Cm3) ≈0.83-85
Flowing speed 15~43 second

Zinc Oxide
Zinc OxidePurpose:
This is a chemical compound with the formula ZnO. Crystalline zinc oxide exhibits the piezoelectric effect and is thermo chromic, changing from white to yellow when heated.
Zirconium Silicate
ZircomiumPurpose:
Zirconium silicate is used in production of some ceramics, enamels, and ceramic glazes. In enamels and glazes it serves as an opacifier.